Zn-Al Alloy Metallized BOPP Film with Heavy Edge for Capacitors

• Customization: Available
• Application: Electronic device, Film for Capacitor Use
• Color: Black
• Model NO.: MPPZn/Al
• Installation Method: Wound Into Capacitor Core
• Material: Polyethylene
• Maximum Voltage: <10KV
• Thermal Rating: E 120
• Thickness: 2.0μm- 12μm
• UV Protection: No
• Hardness: Soft
• Processing Type: Vacuum Coating
• Width: 30mm/37.5mm/50mm/62.5mm/75mm/100mm/125mm etc
• Od(mm): 180mm/200mm/220mm/240mm/250mm/320mm/330mm etc
• Margin Types: Single Margin, Center Margin,Two Margin,etc
• Margin: 0.5mm/1.0mm/1.5mm/2.0mm/2.5mm/5mm etc
• Slitting: Straight Cut or Wave Cut
• MOQ: 10 Kgs
• Elongation at Break: 20~200%
• Density: 0.905±0.005 g/cm3
• Transparency: Opaque
• Normal Resistance: 2-4/6-9ohm/Sq
• ID(mm): 75mm+1/-0.5mm
• Types of Metallized Layer: Al/Zn Metallized Film, Al Metallized Film
• Transport Package: Standard Export Catron Package
• Specification: MPP, MPET
• Origin: China
• HS Code: 3920209090
• Production Capacity: 10000kgs/Month
• Package Size: 37.00cm * 30.00cm * 30.00cm
• Package Gross Weight: 10.000kg

Product Description

Product Description

 

Storage
Metallized film should be stored in its original package with temperature 5 - 35ºC and humidity less than 85%RH before using.

Metallized layer is easily oxidized when exposure to moisture. Therefore, the film should be used as soon as possible when opened.

The recommended temperature is 15 -25ºC with humidity less than 60%RH after opening.

With original sealed package, and stored as mentioned above, the storage time can be as following:
•Al metallized film: 12 months from the delivery date. 
•Al/Zn Alloy metallized film: As zinc is quite unstable , the storage period (from delivery date) depends on the resistance of the film:
≤10 Ω/: 6 months
10 ~30Ω/: 3 months
>30Ω/: 1month